DD Bio ZW iso color – High Strength (3Y-TZP-A)
Pre-colored DD Bio ZW iso color blanks combine the excellent properties of white blanks with the advantage of rapid processing. The ceramic veneering is optimally supported by the primers.
perfectly suitable for:
- Aesthetic veneering of crowns and bridges
- Hybrid-Abutments
1.150 ±200
MPa
5
Universal shades
Indications
Consult instructions for use
Zirconium dioxide constructions made of already pre-shaded blanks may only be treated with DD Art Elements and not additionally with DD Basic Shade, DD Pro Shade Z.
Physical specifications
| Characteristic | Unit | Value |
|---|---|---|
| CTE (25 – 500°C) |
[10-6 K-1] |
~ 10.8 |
| Chem. solubility | [µm/cm2] | ≤ 9.1 |
| Fracture toughness (KIC) | [MPa√m] | > 9.5 |
| Flexural strength* |
[MPa] |
1150 ± 200 |
*measured according to DIN EN ISO 6872
DD Bio ZW iso color according to VITA® for open systems ∅ 98,5mm
| Art. no. | VITA® color | Height (mm) | |
|---|---|---|---|
| G520A10 | A1 | 10 | |
| G522A10 | A1 | 14 | |
| G524A10 | A1 | 18 | |
| G525A10 | A1 | 20 | |
| G526A10 | A1 | 25 | |
| G520A20 | A2 | 10 | |
| G522A20 | A2 | 14 | |
| G524A20 | A2 | 18 | |
| G525A20 | A2 | 20 | |
| G526A20 | A2 | 25 | |
| G520A30 | A3 | 10 | |
| G522A30 | A3 | 14 | |
| G524A30 | A3 | 18 | |
| G525A30 | A3 | 20 | |
| G526A30 | A3 | 25 | |
| G520A350 | A3,5 | 10 | |
| G522A350 | A3,5 | 14 | |
| G524A350 | A3,5 | 18 | |
| G525A350 | A3,5 | 20 | |
| G526A350 | A3,5 | 25 | |
| G520B10 | B1 | 10 | |
| G522B10 | B1 | 14 | |
| G524B10 | B1 | 18 | |
| G525B10 | B1 | 20 | |
| G526B10 | B1 | 25 | |
| G520B20 | B2 | 10 | |
| G522B20 | B2 | 14 | |
| G524B20 | B2 | 18 | |
| G525B20 | B2 | 20 | |
| G526B20 | B2 | 25 | |
| G520C10 | C1 | 10 | |
| G522C10 | C1 | 14 | |
| G524C10 | C1 | 18 | |
| G525C10 | C1 | 20 | |
| G526C10 | C1 | 25 | |
| G520D20 | D2 | 10 | |
| G522D20 | D2 | 14 | |
| G524D20 | D2 | 18 | |
| G525D20 | D2 | 20 | |
| G526D20 | D2 | 25 | |
DD Bio ZW iso color for open systems Ø 98,5mm
| Art. no. | Color | VITA® color | Height (mm) | |
|---|---|---|---|---|
| G 520.500.0 | 500 | A1﹒A2 | 10 | |
| G 522.500.0 | 500 | A1﹒A2 | 14 | |
| G 524.500.0 | 500 | A1﹒A2 | 18 | |
| G 525.500.0 | 500 | A1﹒A2 | 20 | |
| G 526.500.0 | 500 | A1﹒A2 | 25 | |
| G 520.800.0 | 800 | A3﹒B3 | 10 | |
| G 522.800.0 | 800 | A3﹒B3 | 14 | |
| G 524.800.0 | 800 | A3﹒B3 | 18 | |
| G 525.800.0 | 800 | A3﹒B3 | 20 | |
| G 526.800.0 | 800 | A3﹒B3 | 25 | |
| G 520.1000.0 | 1000 | C2﹒C3 | 10 | |
| G 522.1000.0 | 1000 | C2﹒C3 | 14 | |
| G 524.1000.0 | 1000 | C2﹒C3 | 18 | |
| G 525.1000.0 | 1000 | C2﹒C3 | 20 | |
| G 520.1333.0 | 1333 | A3,5﹒B4 | 10 | |
| G 522.1333.0 | 1333 | A3,5﹒B4 | 14 | |
| G 524.1333.0 | 1333 | A3,5﹒B4 | 18 | |
| G 525.1333.0 | 1333 | A3,5﹒B4 | 20 | |
| G 526.1333.0 | 1333 | A3,5﹒B4 | 25 | |
| G 520.2000.0 | 2000 | A4 | 10 | |
| G 522.2000.0 | 2000 | A4 | 14 | |
| G 524.2000.0 | 2000 | A4 | 18 | |
| G 525.2000.0 | 2000 | A4 | 20 | |
| G 526.2000.0 | 2000 | A4 | 25 | |
Chemical composition [wt.%]
|
ZrO₂ + HfO₂ + Y₂O₃ |
≥ 99 |
| Y₂O₃ | < 6 |
|
Al₂O₃ |
< 0.5 |
|
Other oxides |
< 1.0 |