DD cubeX²® ML – Super High Translucent (5Y-TZP)
multilayer – cubic zirconia system
Based on the “DD cubeX²® – cubic zirconia system®” the blanks offer a flowing color gradation from cervical to incisal. The manufacture of aesthetic monoliths has never been this efficient before.
-
High aesthetic monolithic crowns and bridges (up to 3-units)
-
Especially for monolithic anterior restorations (bridges up to 3-units)
-
Cut back (one layer)
-
High aesthetic veneering
Indications
Consult instructions for use
Zirconium dioxide constructions made of already pre-shaded blanks may only be treated with DD Art Elements and not additionally with DD Basic Shade, DD Pro Shade Z.
Not all products are available in every country.
Physical specifications
| Characteristic | Unit | Value |
|---|---|---|
| CTE (25 – 500°C) |
[10-6 K-1] |
~ 10.2 |
| Chem. solubility | [µm/cm2] | ≤ 2.9 |
| Fracture toughness (KIC) | [MPa√m] | > 4.0 |
| Flexural strength* |
[MPa] |
700 ± 100 |
*measured according to DIN EN ISO 6872
DD cubeX²® ML for open systems Ø 98,5 mm
| Art. no. | VITA® color | Height (mm) | |
|---|---|---|---|
| G852017 | Bleach | 14 | |
| G854017 | Bleach | 18 | |
| G856017 | Bleach | 22 | |
| G852007 | A1 | 14 | |
| G854007 | A1 | 18 | |
| G856007 | A1 | 22 | |
| G852001 | A2 | 14 | |
| G854001 | A2 | 18 | |
| G856001 | A2 | 22 | |
| G852002 | A3 | 14 | |
| G854002 | A3 | 18 | |
| G856002 | A3 | 22 | |
| G852003 | A3,5 | 14 | |
| G854003 | A3,5 | 18 | |
| G856003 | A3,5 | 22 | |
| G852009 | A4 | 14 | |
| G854009 | A4 | 18 | |
| G856009 | A4 | 22 | |
| G852008 | B1 | 14 | |
| G854008 | B1 | 18 | |
| G856008 | B1 | 22 | |
| G852004 | B2 | 14 | |
| G854004 | B2 | 18 | |
| G856004 | B2 | 22 | |
| G852010 | B3 | 14 | |
| G854010 | B3 | 18 | |
| G856010 | B3 | 22 | |
| G852011 | B4 | 14 | |
| G854011 | B4 | 18 | |
| G856011 | B4 | 22 | |
| G852012 | C1 | 14 | |
| G854012 | C1 | 18 | |
| G856012 | C1 | 22 | |
| G852005 | C2 | 14 | |
| G854005 | C2 | 18 | |
| G856005 | C2 | 22 | |
| G852013 | C3 | 14 | |
| G854013 | C3 | 18 | |
| G856013 | C3 | 22 | |
| G852014 | C4 | 14 | |
| G854014 | C4 | 18 | |
| G856014 | C4 | 22 | |
| G852015 | D2 | 14 | |
| G854015 | D2 | 18 | |
| G856015 | D2 | 22 | |
| G852006 | D3 | 14 | |
| G854006 | D3 | 18 | |
| G856006 | D3 | 22 | |
| G852016 | D4 | 14 | |
| G854016 | D4 | 18 | |
| G856016 | D4 | 22 | |
Chemical composition [wt.%]
|
ZrO2 + HfO2 + Y2O3 |
≥ 99.0 |
|
Y2O3 |
< 10 |
|
Al2O3 |
≤ 0.01 |
| Other oxides |
< 1.0 |