Deutsch
English
DD Bio ZX² – High Translucent (3Y-TZP-LA)
Through the development of this innovative material, we have combined all the wellknown, positive mechanical properties of “white“ zirconia with an obvious increase in translucence. The DD Bio ZX² concept convinces with its cost effectiveness and also offers all the advantages of full-ceramic zirconia dentures.
Perfectly suitable for:
-
Monolithic crowns and bridges of any span range
-
Especially for monolithic bridges
-
Cut back (one layer)
-
High aesthetic veneering of any span range
3Y-TZP-LA
1.150 ±150
MPa
DD Bio ZX² for open systems Ø 98,5 mm
| Art. no. | Height (mm) |
|---|---|
| G 590 | 10 |
| G 591 | 12 |
| G 592 | 14 |
| G 593 | 16 |
| G 594 | 18 |
| G 595 | 20 |
| G 596 | 25 |
for Sirona inLab® and inLab MC XL-system
| Art. no. | Sizes |
|---|---|
| G 613 | 65x25x22 |
| G 612.1 | 55x19x15,5 |
| G 611 | 40x19x15,5 |
| G 610 | 20x19x15,5 |
Indications
Consult instructions for use
Physical specifications
| Characteristic | Unit | Value |
|---|---|---|
| CTE (25 – 500°C) |
[10-6 K-1] |
~ 10.6 |
| Chem. solubility | [µm/cm2] | ≤ 11 |
| Fracture toughness (KIC) | [MPa√m] | > 8 |
| Flexural strength* |
[MPa] |
1.150 ± 150 |
*measured according to DIN EN ISO 6872
Chemical composition [wt.%]
| ZrO₂ + HfO₂ +Y₂O₃ |
≥ 99.0 |
| Y₂O₃ | < 6 |
|
Al₂O₃ |
≤ 0.15 |
| Other oxides | < 1.0 |