DD Bio ZWiso – High Strength (3Y-TZP-A)

These blanks are distinguished by their enhanced strength and long-term hydrothermal stability. An absolutely homogenous structure is achieved through a specially developed production process. The balanced composition and fine grain structure ensure excellent technical properties.

perfectly suitable for:

  • Aesthetic veneering of crowns and bridges
  • Hybrid-Abutments
3Y-TZP-A
1.150 ±200 MPa

Indikationen

Reduzierte Krone
Reduzierte Brücke (3-gliedrig)
reduzierte Brücke
Hybrid Abutment
Stege
Manual / Gebrauchsanleitung

Consult instructions for use

Physikalische Eigenschaften

Characteristic Unit Value

Density (after sintering)

[g/cm³]

> 6.0

CTE (25 – 500°C)

[10⁻⁶ K⁻¹]

∼ 10.5

Flexural strength*

[MPa]

1300 – 1450

E-Modulus

[GPa]

> 200

*measured according to DIN EN ISO 6872

DD Bio ZW iso for open systems Ø 98,5mm

Art. no. Height (mm)
G 513 10
G 526 12
G 505 14
G 527 16
G 506 18
G 507 20
G 553 25

DD Bio ZS for Sirona inLab® and inLab® MC XL-System

Art. no. Amount Sizes Technic
G 603 25 21x15x15,5
G 600 24 20x19x15,5
G 601 10 40x15x14
G 602 10 40x19x15,5
G 604 2 55x19x15,5

inLab

G 604.1 2 55x19x15,5

MC XL 

G 605 1 65x25x22
G 607 1 85x40x22

Chemische Zusammensetzung [Gew.%]

Characteristic Unit Value
CTE (25 – 500°C)

[10-6 K-1]

~ 10.8
Chem. solubility [µm/cm2] ≤ 9.1
Fracture toughness (KIC) [MPa√m] > 9.5
Flexural strength* 

[MPa]

1.150 ± 200

*measured according to DIN EN ISO 6872

Contact us

Privacy policy
Yes, I have read the Privacy Policy note and I consent that the data provided by me, including the contact data, for the processing of the inquiry and in case of questions are electronically collected and stored. My data will only be used strictly for my request and will not be passed without my consent. This consent can be revoked any time with effect for the future.'
CAPTCHA
This question is for testing whether or not you are a human visitor and to prevent automated spam submissions.